Process for producing epoxy (metha)acrylate

ABSTRACT

The invention provides a process for continuously producing a urethane (meth)acrylate, containing causing a mixed liquid of a compound (A) having a hydroxyl group and a (meth) acryloyl group and a compound (B) having an isocyanate group to pass continuously and densely through a tubular microchannel formed in a heat-conducting reaction device, and reacting the hydroxyl group of the compound (A) with the isocyanate group of the compound (B).

TECHNICAL FIELD

The present invention relates to a production process capable of producing an epoxy (meth)acrylate safely and continuously with good productivity.

BACKGROUND ART

An epoxy (meth)acrylate has hitherto been produced by a batch process using a reaction vessel. In general, an epoxy (meth)acrylate is produced by reacting a carboxyl group of a compound having a carboxyl group and a (meth)acryloyl group with an epoxy group of a compound having an epoxy group. The reaction between a carboxyl group and an epoxy group is exothermic reaction. In the process of the exothermic reaction proceeding, when the temperature of the reaction system is abnormally increased due to accumulation of the reaction heat, the (meth)acryloyl groups are bonded to each other to cause runaway reaction where the reaction product is gelled. Accordingly, for suppressing excessive generation and accumulation of the reaction heat, which bring about runaway reaction, precise temperature control and efficient removal of heat are demanded, but in the case of a large reaction system, such as an industrial production scale, it is difficult to achieve them due to efficiency of agitation, heat removal capability and the like.

The runaway reaction occurring brings about gasification of the unreacted raw materials due to heat generation on the runaway reaction, and gasification due to decomposition of the epoxy (meth)acrylate produced. The phenomena may result in quick increase of the pressure inside the reaction system to cause fatal breakage of the equipment in some cases. For preventing the equipment from being broken, a measure of opening the pressure accumulated in the system and a measure of discharging the contents to the outside of the system are taken by opening a manhole, a relief valve, a rupture disk, an explosion vent or the like provided on the reaction vessel. However, the measures require large-scaled equipments, which bring about an increased investment cost and a large occupied area, and thus only poor productivity is obtained.

A method of adding a polymerization inhibitor is known as a measure for terminating runaway reaction occurring during production of an epoxy (meth)acrylate. It is necessary in the method that a polymerization inhibitor is dispersed and dissolved in the reaction system in a very short period of time.

However, the reaction system is liable to be increased in viscosity upon gelling, which bring about such a problem that it is considerably difficult to disperse and dissolve a polymerization inhibitor in the reaction system in a very short period of time. In addition, the driving capacity of the agitation blade for agitating the reaction system becomes insufficient against the quick increase of the viscosity due to the runaway reaction, which results in not only the failure of sufficient dispersion and dissolution of the polymerization inhibitor in the reaction system, but also such a problem that the equipment suffer fatal breakage, such as malfunction of the agitating device due to application of load. The problem becomes serious in the case where a diluent solvent or the like is not used upon producing an epoxy (meth)acrylate.

As a measure for facilitating dispersion and dissolution of a polymerization inhibitor in a reaction system, such a method may be used that a polymerization inhibitor is used after dissolving in a solvent or the like, but for addressing occurrence of runaway reaction, it is necessary to prepare in advance a large amount of a solution containing a polymerization inhibitor dissolved in a solvent. Accordingly, the cost of production of an epoxy (meth)acrylate is increased. A polymerization inhibitor contains a mutagenic substance and thus is necessarily handled with adequate care.

As a measure for suppressing runaway reaction from occurring upon production of an epoxy (meth)acrylate, such a method has been known that a solvent is made present in the reaction system, thereby decreasing the concentration of the polymerizable compound in the system and simultaneously decreasing the viscosity of the fluid, which is increased associated with the progress of the reaction, for enhancing the controllability of the reaction. In the method, however, the solvent is necessarily recovered after completing the reaction, and the yield ratio per reaction vessel is decreased due to the use of the solvent, which impair the productivity. Furthermore, the resin composition thus obtained may have a problem in quality due to the solvent remaining in a slight amount therein.

The production of an epoxy (meth)acrylate may not have good productivity due to the aforementioned measures for addressing runaway reaction. Furthermore, even with the measures for addressing runaway reaction performed, it is the current situation that an epoxy (meth)acrylate is produced with poor efficiency under conditions that do not cause runaway reaction, for example, gradually heating with care about generation of heat, at a low temperature of 150° C. or less, preferably 130° C. or less, for a prolonged period of time of from 3 to 8 hours (see, for example, Patent Document 1).

As a production method capable of preventing heating with the reaction heat, suppressing side reaction, such as multimerization, and providing a high reaction rate, such a method for producing a ring-opening reaction product of an epoxy compound is proposed that an epoxy compound and a compound having a hydroxyl group are caused to pass through a channel having a fluid cross-sectional area of from 300 to 1,000,000 μm² (from 3×10⁴ to 1 mm²), and the compounds are made in contact with each other to perform ring-opening addition reaction (see, for example, Patent Document 2). However, in the production method disclosed in Patent Document 2, for example, a ring-opening reaction product of ethylhexyl alcohol and epichlorohydrin is produced in Example 1, and production of a ring-opening reaction product having a (meth)acryloyl group or the like causing runaway reaction is not considered. Accordingly, Patent Document 2 fails to disclose any measure for preventing runaway reaction in polymerization of a (meth)acryloyl group, which is an issue in the production of an epoxy (meth)acrylate. Furthermore, a long period of 160 minutes is required for reacting the epoxy compound and the compound having a hydroxyl group sufficiently (for example, to a reaction rate of 98%) in the channel, and thus the production efficiency is considerably poor.

Patent Document 1: JP-A-2002-293876

Patent Document 2: JP-A-2006-111574

DISCLOSURE OF THE INVENTION Problems to be Solved by the Invention

An object of the present invention is to provide a process for producing an epoxy (meth)acrylate safely with good productivity.

Means for Solving the Problems

As a result of earnest investigations made by the inventors, it has been found that by using a heat-conducting reaction device having a tubular microchannel formed therein, upon causing a mixed liquid of a compound (A) having a carboxyl group and a (meth)acryloyl group and a compound (B) having an epoxy group to pass continuously and densely through the tubular microchannel, and reacting the carboxyl group of the compound (A) with the epoxy group of the compound (B), the reaction device having a tubular microchannel has a space size making a fluid cross-sectional area, through which the mixed liquid passes densely, of from 0.1 to 4.0 mm², and the reaction liquid is caused to pass through the tubular microchannel to provide a Reynolds number in a range of from 0.4 to 100, whereby mixture by molecular diffusion proceeds associated with a microturbulent flow in the microchannel, the flow in which has been ordinarily considered to be a laminar flow, and thus the compound (A) and the compound (B) are actively in contact with each other, it has also been found that by heating the heat-conducting reaction device to a temperature of from 150 to 260° C., which cannot be employed in an ordinary batch system, the reaction efficiency between the carboxyl group and the epoxy group is enhanced, and the capacity of an epoxy (meth)acrylate discharged from the tubular microchannel after completing the reaction is smaller than that in the batch system and thus can be easily controlled in temperature by continuously cooling, whereby consequently runaway reaction of (meth)acryloyl groups is hard to occur, and an epoxy (meth)acrylate can be produced with good productivity since the reaction occurs in a short period of time. Thus, the invention has been completed.

The invention provides a process for continuously producing an epoxy (meth)acrylate, containing causing a mixed liquid of a compound (A) having a carboxyl group and a (meth)acryloyl group and a compound (B) having an epoxy group to pass continuously and densely through a tubular microchannel formed in a heat-conducting reaction device, and reacting the carboxyl group of the compound (A) with the epoxy group of the compound (B),

the tubular microchannel in the reaction device having a space size making a fluid cross-sectional area, through which the mixed liquid passes densely, of from 0.1 to 4.0 mm², and the process containing heating the heat-conducting reaction device to a temperature of from 150 to 260° C., reacting the mixed liquid to provide a Reynolds number of a reaction liquid passing through the tubular microchannel in a range of from 0.4 to 100, and after completing reaction, cooling continuously a reaction product discharged from the heat-conducting reaction device.

Advantages of the Invention

According to the production process of the invention, such a production process can be provided that is capable of producing an epoxy (meth)acrylate safely with good productivity. Furthermore, the process is dispense with large-scaled equipments, and reduction of investment cost and production cost is expected.

BEST MODE FOR CARRYING OUT THE INVENTION

The compound (A) used in the invention has a carboxyl group and a (meth)acryloyl group. The compound (A) is not particularly limited and may be a solid or a liquid having a high viscosity at ordinary temperature as far as it can be fed by such a measure as melting under heat, dissolving or dispersing without clogging the channel, and known compounds may be used therefor.

Examples of the compound (A) used in the invention include acrylic acid, methacrylic acid, a dimer or trimer acid thereof, a half ester compound of a hydroxy(meth)acrylate compound, such as hydroxyethyl (meth)acrylate, hydroxypropyl (meth)acrylate and hydroxybutyl (meth)acrylate, with an acid anhydride, a reaction product of (meth)acrylic acid and caprolactone or the like, and mixtures thereof. These compounds may be used solely or in combination of two or more of them.

In the production process of the invention, acrylic acid or methacrylic acid providing a large heat quantity on reaction with the compound (B) is preferred as the compound (A) since the advantage of the invention, i.e., safe production, can be sufficiently exhibited, and polymerization is facilitated owing to the high acryloyl group concentration thereof.

The compound (B) used in the invention has an epoxy group. The compound (B) is not particularly limited and may be a solid or a liquid having a high viscosity at ordinary temperature as far as it can be fed by such a measure as melting under heat, dissolving or dispersing without clogging the channel, and known compounds may be used therefor.

Examples of the compound (B) used in the invention include an epoxy resin. Examples of the epoxy resin include a bisphenol epoxy resin, a naphthalene epoxy resin, a novolak epoxy resin, such as a cresol-novolak epoxy resin and a phenol-novolak epoxy resin, a halogenated bisphenol epoxy resin, a halogenated novolak epoxy resin, a resin of a glycidyl ester of a polybasic carboxylic acid, an aliphatic epoxy resin, an alicyclic epoxy resin, and polyalkylene glycol diglycidyl ether, allyl glycidyl ether, phenyl glycidyl ether, triglycidyl isocyanurate, derivatives thereof, and a copolymer of a glycidyl group-containing unsaturated monomer, such as polyglycidyl (meth)acrylate and glycidyl (meth)acrylate, with another unsaturated monomer. These compounds may be used solely or in combination of two or more of them.

In the production process of the invention, a compound having an epoxy equivalent of 200 or less providing a large heat quantity on reaction with the compound (A) is preferred as the compound (B) since the advantage of the invention, i.e., safe production, can be sufficiently exhibited. In particular, a bisphenol epoxy resin and a naphthalene epoxy resin, which are aromatic epoxy resins, are preferred as the compound (B) since the compounds facilitate polymerization and provide a large heat quantity upon reaction, thereby attaining sufficiently the advantage of the production process of the invention.

The heat-conducting reaction device used in the process for producing an epoxy (meth)acrylate of the invention has a tubular microchannel formed therein. The mixed liquid of the compound (A) having a carboxyl group and a (meth)acryloyl group and the compound (B) having an epoxy group is caused to pass continuously and densely through the tubular microchannel, and the carboxyl group of the compound (A) is reacted with the epoxy group of the compound (B), thereby producing continuously an epoxy (meth)acrylate. The heat-conductive reaction device used has the tubular microchannel that has a space size making a fluid cross-sectional area, through which a liquid passes densely, of from 0.1 to 4 mm², thereby providing advantages of the invention, for example, the pressure loss does not become too large, good productivity is obtained, clogging of the channel is hard to occur, heating and cooling of the channel can be quickly controlled. The heat-conductive reaction device preferably has the tubular microchannel that has a space size making a fluid cross-sectional area, through which a liquid passes densely, of from 0.3 to 1.0 mm². The term “cross section” referred in the invention means the cross section in the direction perpendicular to the flow direction in the reaction channel, and the term “cross-sectional area” means an area of the cross section.

In the process for producing an epoxy (meth)acrylate of the invention, it is necessary to react the mixed liquid to provide a Reynolds number of a reaction liquid passing through the tubular microchannel in a range of from 0.4 to 100. In general, when a fluid is caused to pass through a tubular microchannel having a space size making a fluid cross-sectional area, through which a liquid passes densely, of from 0.1 to 4 mm², the flowing fluid exhibits a laminar flow. Accordingly, in the case where the mixed liquid of the compound (A) having a carboxyl group and a (meth)acryloyl group and the compound (B) having an epoxy group is caused to pass through the channel, the compound (A) and the compound (B) that are far remote from each other have less occasion of contact and are hard to be reacted. Consequently, only the compound (A) and the compound (B) that are in the vicinity of each other are reacted, but the reaction does not proceed even when the compounds further migrate inside the channel. The inventors have found that when the mixed liquid of the compound (A) and the compound (B) is caused to pass through the tubular microchannel having a space size making a fluid cross-sectional area, through which a liquid passes densely, of from 0.1 to 4 mm² in such a manner that provides a Reynolds number in a range of from 0.4 to 100, such a state is formed in the channel that mixture proceeds associated with a microturbulent flow, thereby activating contact between the compound (A) and the compound (B), and thus the inventors have completed the invention. The Reynolds number is preferably from 1 to 50. In the case where the Reynolds number is less than 0.4, the reaction proceeds too slowly to cause gelation due to the prolonged residence time, and the Reynolds number exceeding 100 is not preferred since the enhancement of the reaction efficiency is limited, and the reactor becomes too long.

The Reynolds number referred in the invention is calculated by the following expression (1). Reynolds number=(D×u×ρ)/μ  (1)

Herein, D is the inner diameter of the channel, u is the average flow velocity, ρ is the density of the fluid, and μ is the viscosity of the fluid. In the invention, the terms in the expression (1) are defined as follows for providing the Reynolds number.

D (inner diameter of channel): equivalent diameter of the tubular microchannel (m)

u (average flow velocity): flow velocity (m/sec) of the mixed liquid of the compound (A) and the compound (B)

ρ (density of fluid): density of water at 20° C. (998.2 kg/m³)

μ (viscosity of fluid): viscosity of water at 20° C. (1.002 mPa·s)

In the process for producing an epoxy (meth)acrylate of the invention, it is necessary to heat the heat-conducting reaction device to a temperature of from 150 to 260° C. Such an advantageous effect is obtained by selecting the temperature that the reaction between the carboxyl group and the epoxy group is performed with good efficiency while preventing runaway reaction, which is polymerization of the (meth)acryloyl group, from occurring. The temperature of the heat-conducting reaction device is preferably from 160 to 240° C., and more preferably from 170 to 220° C., since the runaway reaction is hard to occur, and a good production efficiency is obtained.

In the process for producing an epoxy (meth)acrylate of the invention, the cross-sectional area of the fluid passing the microchannel of the reaction device used in the invention, the Reynolds number of the mixed liquid passing through the microchannel, and the temperature of the heat-conducting reaction device are selected in the aforementioned manners, whereby the carboxyl group and the epoxy group undergo efficient reaction, and consequently, an epoxy (meth)acrylate thus produced can be cooled before occurrence of polymerization reaction of the (meth)acryloyl groups. The flow velocity upon causing the mixed liquid to pass through the microchannel is preferably from 1.8×10⁻⁴ to 0.28 m/sec, and more preferably from 4.5×10⁻⁴ to 0.14 m/sec.

The heat-conducting reaction device used in the invention is not particularly limited in other requirements than that the reaction device has a heat exchange function and has a tubular microchannel having a space size making a fluid sectional area, through which a liquid passes densely, of from 0.1 to 4 mm². Examples of the device include a device having the aforementioned channel (which may be hereinafter referred simply to as “microchannel”) in a member, which is used as a device for chemical reaction.

The cross-sectional shape obtained by cutting perpendicularly the flow of the mixed liquid containing the compound (A) and the compound (B) in the tubular microchannel may be a square shape, a rectangular shape, a trapezoidal or parallelogram shape, a triangular shape, a polygonal shape including a pentagonal shape (including a shape obtained by rounding the corners thereof and a shape having a high aspect ratio, i.e., a slit shape), an astral shape, and a circular shape including a hemicircular shape and an elliptical shape, or the like. The cross-sectional shape of the microchannel may not be necessarily constant thereover.

The method for forming the tubular microchannel is not particularly limited, and in general is formed in such a manner that a member (X) having a trench formed on a surface thereof is fixed through the surface having the trench to another member (Y) by lamination, adhesion or the like, thereby forming the microchannel as a space between the member (X) and the member (Y).

In the case where the tubular microchannel is formed between the member (X) and the member (Y), the member (X) may have a heat exchange function. For example, a trench, through which a temperature controlling liquid flows, is formed on the surface of the member (X), and another member is fixed to the surface having the trench, through which a temperature controlling liquid flows, by adhesion, lamination or the like. In general, the member (X) having a trench on the surface thereof and the member (Y) having a trench, through which a temperature controlling liquid flows, are adhered through the surface having the trench of the member (X) and the surface of the member (Y) opposite to the surface having the trench fixed to each other, thereby forming the channel, and the plural members (X) and the plural members (Y) are fixed alternately to each other.

In this case, the trench may be formed as a dent having a height lower than the surrounding or may be formed as a gap between walls standing on the surface of the member. The trench may be formed on the surface of the member in an arbitrary method, and examples of the method that can be employed include an injection molding method, a solvent casting method, a melt replication method, cutting, etching, photolithograph (including energy ray lithography), and laser abrasion.

The layout of the channel in the member may be linear, branched, comb form, curve, spiral, zigzag or any other arbitrary arrangement depending on purposes.

The channel may be connected, for example, to a mixing field, an extraction field, a separation field, a flow rate measuring part, a detecting part, a liquid storage tank, a membrane separation mechanism, a connection port to the inside or outside of the device, a connection path, an expansion path of chromatography or cataphoresis, a part of a valve mechanism (a peripheral part of a valve), a pressurizing mechanism and a depressurizing mechanism.

The outer shape of the member is not particularly limited and may be any shape depending on purposes. Examples of the shape of the member include a plate shape, a sheet shape (including a film shape, a ribbon shape and the like), a coated film shape, a bar shape, a tube shape and another molded material having a complicated shape. The outer dimension including the thickness and the like is preferably constant thereover. An arbitrary material may be used for the member, and examples thereof include a polymer, glass, ceramics, a metal and a semiconductor.

The heat-conducting reaction device used in the invention is preferably such one that is produced by fixing the member (X) having a trench on the surface thereof with the other member (Y) on the surface having the trench by lamination, adhesion or the like, thereby forming the tubular microchannel as a space between the member (X) and the member (Y). Examples of the heat-conducting reaction device include such one that has a structure containing plural heat-conducting plate structures each having plural trenches on the surface thereof, which are laminated on each other.

The channel formed in the aforementioned manner is a space formed between the members by combining at least two members, and in alternative, a simple tube or a member having a tubular shape may be used as the reaction channel. The length of the channel may be appropriately determined for providing a desired reaction rate, and is generally from 0.5 to 100 m, and preferably from 3 to 70 m.

Examples of the heat-conducting reaction device used in the production process of the invention include such a device that is produced by laminating alternately a heat-conducting plate structure having the tubular microchannel provided therein and a heat-conducting plate structure having a channel, through which a liquid for heat exchanging with the mixed liquid passes. A mixing space for mixing the compound (A) and the compound (B) separately fed may be provided preceding the device or inside the device. It is preferred in the invention that the compound (A) and the compound (B) are preferably fed as a mixed liquid formed by mixing in advance to the heat-conducting reaction device continuously.

The heat-conducting reaction device having the tubular microchannel formed inside used in the invention will be specifically described below. FIG. 1 is a schematic illustration showing an example of a chemical reaction device 1 having a tubular microchannel having a space size making a fluid sectional area, through which a liquid passes densely, of from 0.1 to 4 mm², which is a reaction device containing plates each having the tubular microchannel, through which the mixed liquid passes, and plates each having a channel, through which a liquid for heat exchanging with the mixed liquid passes, laminated alternately.

The chemical reaction device 1 in FIG. 1 is constituted by laminating alternately plural first plates (2 in FIG. 1) and plural second plates (3 in FIG. 1) having the same rectangular plate shape. Each one of the first plates have a channel having the cross-sectional area of from 0.1 to 4.0 (mm²) (which is referred hereinafter to as a reaction channel) (hereinafter, the plate having the reaction channel is referred to as a process plate). The second plate has a channel for a temperature controlling liquid (which is hereinafter referred to as a temperature controlling channel) (the plate having the temperature controlling channel is hereinafter referred to as a temperature controlling plate). As shown in FIG. 2, inlet ports and outlet ports thereof are disposed by scattering in each areas including the end surfaces 1 b and 1 c and the side surfaces 1 d and 1 e of the chemical reaction device 1, and connecting parts 32 each containing a connector 30 and a joint part 31 are connected to the areas for causing the compound (A) and the compound (B), and the temperature controlling liquid to pass through, respectively.

Through the connecting parts, a liquid a (mixed liquid) containing the compound (A) and the compound (B) is fed to the end surface 1 b, a liquid β containing a reaction product between the compound (A) and the compound (B) is discharged from the end surface 1 c, and the temperature controlling liquid γ is fed to the side surface 1 e and discharged from the side surface 1 d.

The shape in plane view of the chemical reaction device 1 is not limited to the rectangular shape as shown in the figure, and may be a square shape or a rectangular shape having a longer distance between the side surfaces 1 d and 1 e than the distance between the end surfaces 1 b and 1 c. In the following description, for simplification, the direction from the end surface 1 b toward the end surface 1 c refers to the longitudinal direction of the process plates and the temperature controlling plates of the chemical reaction device 1, and the direction from the side surface 1 d toward the side surface 1 e refers to the transverse direction of the process plates and the temperature controlling plates of the chemical reaction device 1, according to the configuration shown in the figure.

As shown in FIG. 3, the process plate has on one surface 2 a thereof plural channels 4 each having a concave trench cross-sectional shape that penetrate in the longitudinal direction of the process plate and are arranged in the transverse direction with a prescribed interval p₀. The length of the channel 4 is designated as L. The cross-sectional shape has a width w₀ and a depth d₀.

The cross-sectional shape of the channel 4 can be appropriately determined corresponding to the kind and the flow rate of the liquid α containing the compound (A) and the compound (B) and the length L of the channel, and the width w₀ and the depth d₀ are set in a range of from 0.1 to 16 (mm) and a range of from 0.1 to 2 (mm), respectively, for ensuring homogeneity of the temperature distribution within the cross section thereof. The values of the width and the depth mentioned are those disclosed in the figure, and can be appropriately interpreted to make a wider value with respect to the heat-conducting surface. The number of channels is not particularly limited and is, for example, from 1 to 1,000, and preferably from 10 to 100, per one plate.

The liquid α are caused to flow within each of the channels 4, and as shown in FIGS. 1 to 3, is fed from the side of the one end surface 2 b and discharged to the side of the other end surface 2 c.

As shown in FIG. 1, the temperature controlling plate has on one surface 3 a thereof temperature controlling channels 6 each having a concave trench cross-sectional shape provided with a prescribed distance. The cross-sectional area of the temperature controlling channel 6 is not particularly limited as far as heat can be conducted to the reaction channels and is generally in a range approximately from 0.1 to 4.0 (mm²), and more preferably from 0.3 to 1.0 (mm²). The number of the temperature controlling channels 6 may be appropriately determined in consideration of the heat exchange efficiency without particular limitation, and is, for example, from 1 to 1,000, and preferably from 10 to 100, per one plate.

As shown in FIGS. 1 and 3, the temperature controlling channel 6 may contain plural main channels 6 a disposed along the longitudinal direction of the temperature controlling plate, and a feed-side channel 6 b and a discharge-side channel 6 c disposed on the upstream side and the downstream side of the main channels 6 a, respectively, substantially perpendicular to the channels 4 and connected to the main channels 6 a. In FIGS. 1 and 3, the feed-side channel 6 b and the discharge-side channel 6 c each are turned at a right angle twice and are opened to the outside at the side surfaces 3 d and 3 e of the temperature controlling plate, respectively. With respect to the number of the channels of the temperature controlling channel 6, plural channels are disposed only for the main channels 6 a of the temperature controlling channel 6, and the feed-side channel 6 b and the discharge-side channel 6 c each are constituted by only one channel.

The main channels 6 a of the temperature controlling channel 6 are provided in the transverse direction of the temperature controlling plate with respect to the channels 4 in an area overlapping in the lamination direction the area where the channels 4 are distributed.

It is preferred that the main channels 6 a are each disposed in the lamination direction between the channels 4 and 4 adjacent to each other, and it is more preferred that the main channels 6 a are each disposed to overlap in the lamination direction each of the channels 4.

The plural process plates and the plural temperature controlling plates are laminated and fixed alternately with the process plates and the temperature controlling plate being in the same direction.

In the embodiment of the chemical reaction device 1, accordingly, the channels 4 and the temperature controlling channels 6 are covered with the lower surface of the plate laminated with the open surface of a concave trench thereof upward, thereby forming a tunnel shape having a rectangular cross section with both ends open.

The process plates and the temperature controlling plates may be produced with an appropriate metallic material, and for example, can be produced by etching a stainless steel plate to form the channels 4, the temperature controlling channels 6 and the like, and subjecting the surface of the channels to electrolytic polishing.

Examples of an apparatus that is equipped with a chemical reaction device having the channels used in the production process of the invention include a production apparatus shown in FIG. 4. Specifically, a production apparatus having a chemical reaction device shown below is exemplified.

Chemical Reaction Device

The chemical reaction device has the structure shown in FIG. 1, and the structure contains process plates and temperature controlling plates laminated alternately. The process plates each have channels 4 formed therein, and the temperature controlling plates each have temperature controlling channels 6 formed therein.

The chemical reaction device 40 used in the production apparatus shown in FIG. 4 contains 3 plies of process plates each having 20 reaction channels 4 formed by dry etching and 4 plies of temperature controlling plates each having 20 temperature controlling channels 6 formed by dry etching laminated alternately. The process plates 2 and the temperature controlling plates 3 each are formed of SUS304 as a material, and each have a thickness of 1 mm. The reaction channels 4 and the temperature controlling channels 6 each have a cross sectional dimension of 1.2 mm in width and 0.5 mm in depth.

The chemical reaction device 50 used in the production apparatus shown in FIG. 4 contains 2 plies of process plates each having 5 reaction channels 4 formed by dry etching and 3 plies of temperature controlling plates each having 5 temperature controlling channels 6 formed by dry etching laminated alternately. The process plates 2 and the temperature controlling plates 3 each are formed of SUS304 as a material, and each have a thickness of 1 mm. The reaction channels 4 and the temperature controlling channels 6 each have a cross sectional dimension of 1.2 mm in width and 0.5 mm in depth.

The chemical reaction device 60 used in the production apparatus shown in FIG. 4 contains 20 plies of process plates each having 20 reaction channels 4 formed by dry etching and 21 plies of temperature controlling plates each having 20 temperature controlling channels 6 formed by dry etching laminated alternately. The process plates 2 and the temperature controlling plates 3 each are formed of SUS304 as a material, and each have a thickness of 1 mm. The reaction channels 4 and the temperature controlling channels 6 each have a cross sectional dimension of 1.2 mm in width and 0.5 mm in depth.

In FIG. 4, pipes, through each of which the compound (A) and the compound (B) pass respectively, are extended from an outlet port of a syringe pump 63 for storing the compound (A) (61) and an outlet port of a syringe pump 64 for storing the compound (B) (62), respectively, and the pipes are connected to an inlet port of a mixer (i.e., a mixing space for mixing the compound (A) and the compound (B)) 65.

The compound (A) (61) and the compound (B) (62) are mixed in the mixer 65, thereby forming a mixed liquid containing the compound (A) (61) and the compound (B) (62). The liquid moves to an inlet port 1 b of the chemical reaction device 40, 50 or 60 through a pipe connected to an outlet port of the mixer 65. A temperature controlling unit 66 is connected to the chemical reaction device 40, 50 or 60. The compound (A) and the compound (B) in the mixed liquid are reacted with each other while moving in the microchannel of the chemical reaction device 40, 50 or 60. The liquid moves within the microchannel of the chemical reaction device 40, 50 or 60 and reaches an outlet port 1 c of the chemical reaction device 40, 50 or 60. Thereafter, the liquid moves to an inlet port of a cooling heat exchange device 67 for cooling through a pipe connected to the outlet port.

In the production process of the invention, the reaction is preferably performed by using a reaction device containing plural heat-conducting reaction devices connected in series each having a tubular microchannel formed therein, such as the chemical reaction device 40, 50 or 60, since the Reynolds number and the temperature can be respectively changed. The compound (A) and the compound (B) may be each stored in separate syringe pumps, as described above, and may be agitated in a mixer to form a mixed liquid, and the compound (A) and the compound (B) may also be mixed to form a mixed liquid in advance, which may be stored in one syringe pump and fed to the chemical reaction device.

After providing an epoxy (meth)acrylate in the aforementioned manner, the reaction product obtained is discharged from the heat-conducting reaction device. The reaction product is then cooled continuously, under a temperature condition of from 50 to 90° C., more preferably 70° C. The reaction product is cooled quickly and continuously, thereby preventing runaway reaction of the (meth)acryloyl group from occurring. The cooling operation may be performed by natural air cooling in the air, by placing the discharged product quickly in a solvent for cooling, or by causing the product to pass through a cooling device having a heat exchange function. It is preferred in the invention that the product is preferably cooled by causing to pass through a cooling device having a heat exchange function. The cooling device is preferably a cooling heat exchange device having a tubular microchannel formed therein.

The continuous cooling operation with the cooling heat exchange device is preferably performed, for example, by causing the reaction product to pass continuously through the cooling heat exchange device having a tubular microchannel formed therein connected to the exit of the reaction liquid (i.e., the outlet port) of the heat-conducting reaction device.

Specifically, the liquid β containing the reaction product of the compound (A) (61) and the compound (B) (62) (i.e., an epoxy (meth)acrylate) moving to an inlet port of the cooling heat exchange device (i.e., the cooling device) 67 is cooled while moving in the cooling heat exchange device 67, and reaches an outlet port of the cooling heat exchange device 67. The liquid β is discharged from the cooling heat exchange device 67 through a pipe connected to the outlet port and then discharged to a receiving vessel 70 through an valve 69.

Preferred examples of the cooling heat exchange device used in the invention include a heat-conducting reaction device having a tubular microchannel formed therein, which is preferably used as the heat-conducting reaction device, i.e., one having plural heat-conducting plate structures each having plural trenches formed on the surface thereof laminated on each other. Examples of the apparatus include an apparatus having the chemical reaction device.

The reaction between the compound (A) and the compound (B) in the tubular microchannel may be terminated at an arbitrary yield, and the reaction product and the unreacted materials may be discharged to the outside of the reaction channel. In general, the viscosity of the reaction product is increased with progress of the reaction, and in consideration of the pressure loss, such an operation may be, for example, employed that the reaction until the initial stage or the intermediate stage of reaction is performed by the production process of the invention, and subsequently, the composition containing the unreacted materials is placed in a reactor or a storage tank for batch reaction or placed in a channel having a larger cross-sectional area, thereby reacting the remaining unreacted materials.

The compound (A) and the compound (B) used in the production process of the invention each may be a liquid having a viscosity capable of being fed, and may be heated or dissolved in and diluted with a solvent for enabling the feeding.

The compound (A) and the compound (B) each may contain, depending on necessity, an additive, such as a catalyst (initiator) and a polymerization inhibitor in such an extent that the channel is not clogged.

The compound (A) and the compound (B) used in the invention may be fed to the channel individually or in a mixed state as far as the reaction is adversely affected. The compounds may be diluted with a solvent and may contain an additive, such as a catalyst (initiator) and a polymerization inhibitor, depending on necessity.

The catalyst (initiator) is not particularly limited as far as it can be dissolved in the compound (A) and the compound (B) or dispersed therein in such an extent that the channel is not clogged, or can be used after dissolving in a solvent, and a known catalyst (initiator) may be used, examples of which include a phosphine compound, such as triphenylphosphine, an amine compound, such as triethylamine, a quaternary ammonium salt, such as tetramethylammonium salt and benzyltrimethylammonium salt, a quaternary phosphonium salt, and an imidazole compound, such as 2-methylimidazole and 2-methyl-4-methylimidazole.

The polymerization inhibitor is not particularly limited as far as it can be dissolved in the compound (A) and the compound (B) or dispersed therein in such an extent that the channel is not clogged, or can be used after dissolving in a solvent, and a known polymerization inhibitor may be used, examples of which include methoquinone, hydroquinone, 1,4-naphthoquinone, phenothiazine, t-butylhydroquinone and aluminum N-nitrophenylhydroxyamine.

EXAMPLE

The invention will be described in more detail with reference to examples below. The percentages in the examples are by weight unless otherwise indicated.

Chemical Reaction Device Used in Examples and Comparative Examples

A chemical reaction device having the structure shown in FIG. 1 was used in the example. The structure contains process plates 2 and temperature controlling plates 3 laminated alternately. The process plates each have a channel 4 formed therein, and the temperature controlling plates each have a temperature controlling channel 6 formed therein. As the chemical reaction device, chemical reaction devices 40 and 50 shown in FIG. 4 exhibiting different Reynolds numbers on the same flow rate (on the same flow velocity) were used.

The chemical reaction device 40 contains 3 plies of process plates each having 20 reaction channels 4 formed by dry etching and 4 plies of temperature controlling plates each having 20 temperature controlling channels 6 formed by dry etching laminated alternately. The process plates 2 and the temperature controlling plates 3 each are formed of SUS304 as a material, and each have a thickness of 1 mm. The reaction channels 4 and the temperature controlling channels 6 each have a cross sectional dimension of 1.2 mm in width and 0.5 mm in depth. The reaction channels 4 each have a length of 80 mm.

The chemical reaction device 50 contains 2 plies of process plates each having 5 reaction channels 4 formed by dry etching and 3 plies of temperature controlling plates each having 5 temperature controlling channels 6 formed by dry etching laminated alternately. The process plates 2 and the temperature controlling plates 3 each are formed of SUS304 as a material, and each have a thickness of 1 mm. The reaction channels 4 and the temperature controlling channels 6 each have a cross sectional dimension of 1.2 mm in width and 0.5 mm in depth. The reaction channels 4 each have a length of 40 mm.

The chemical reaction device 50 was used as the cooling heat exchange device 67.

Example 1

A production apparatus 80 shown in FIG. 4 having one chemical reaction device 40 connected was used. 737 g of a bisphenol A epoxy resin (epoxy equivalent: 189), 277 g of acrylic acid, 5.1 g of triphenylphosphine as a catalyst, and 0.5 g of methoquinone as a polymerization inhibitor were mixed and dissolved in advance to prepare a mixed solution 61.

The mixed solution 61 was continuously caused to flow with the syringe pump 63 through the mixer 65, the chemical reaction device 40, the cooling heat exchange device 67 and the exhaust pressure valve 69 to make a Reynolds number, during passing through the channels formed at the process plates in the chemical reaction device 40, of 1.24, and the reaction mixture thus discharged was received by the receiving vessel 70. In the chemical reaction device 40, a temperature controlling liquid (oil) at 180° C. was caused to flow continuously through the temperature controlling channel 6 of the temperature controlling plate by the temperature controlling unit 66. In the cooling heat exchange device 67, warm water at 70° C. was caused to flow continuously by the temperature controlling unit 68. The reaction was performed at a pressure in the tube of 1 MPa or more controlled by the exhaust pressure valve 69.

The result of quantitative determination of unreacted acrylic acid in the reaction mixture terms of acid value revealed that epoxy acrylate was formed at a reaction rate of 34% with a reaction time of 63 seconds. No runaway reaction occurred. The reaction time referred herein means the total period of time, over which the mixed liquid of the compound (A) and the compound (B) is retained in the chemical reaction device (hereinafter the same).

Example 2

A production apparatus 80 shown in FIG. 4 having 6 chemical reaction devices 50 connected was used. 737 g of a bisphenol A epoxy resin (epoxy equivalent: 189), 277 g of acrylic acid, 5.1 g of triphenylphosphine as a catalyst, and 0.5 g of methoquinone as a polymerization inhibitor were mixed and dissolved in advance to prepare a mixed solution 61.

The mixed solution 61 was continuously caused to flow with the syringe pump 63 through the mixer 65, the chemical reaction device 50, the cooling heat exchange device 67 and the exhaust pressure valve 69 to make a Reynolds number, during passing through the channels formed at the process plates in the chemical reaction device 50, of 1.75, and the reaction mixture thus discharged was received by the receiving vessel 70. In each of the chemical reaction devices 50, a temperature controlling liquid (oil) at 180° C. was caused to flow continuously through the temperature controlling channel 6 of the temperature controlling plate by the temperature controlling unit 66. In the cooling heat exchange device 67, warm water at 70° C. was caused to flow continuously by the temperature controlling unit 68. The reaction was performed at a pressure in the tube of 1 MPa or more controlled by the exhaust pressure valve 69.

The result of quantitative determination of unreacted acrylic acid in the reaction mixture in terms of acid value revealed that epoxy acrylate was formed at a reaction rate of 86.4% with a reaction time of 135 seconds. No runaway reaction occurred.

Example 3

A reaction mixture was obtained in the same manner as in Example 2 except that the Reynolds number was 3.72. The result of quantitative determination of unreacted acrylic acid in the reaction mixture revealed that epoxy acrylate was formed at a reaction rate of 92.3% with a reaction time of 63 seconds. No runaway reaction occurred.

Example 4

A reaction mixture was obtained in the same manner as in Example 2 except that the Reynolds number was 7.44. The result of quantitative determination of unreacted acrylic acid in the reaction mixture revealed that epoxy acrylate was formed at a reaction rate of 86% with a reaction time of 32 seconds. No runaway reaction occurred.

Example 5

A reaction mixture was obtained in the same manner as in Example 2 except that the Reynolds number was 2.62. The result of quantitative determination of unreacted acrylic acid in the reaction mixture revealed that epoxy acrylate was formed at a reaction rate of 99% with a reaction time of 90 seconds. No runaway reaction occurred.

The reaction rate was 99% with a transit time of 90 seconds, and thus the reaction was substantially completed. No runaway reaction occurred at such a reaction temperature that had not been achieved by a reaction vessel, and the reaction time was shortened to such an extent that had not been achieved by a reaction vessel.

The epoxy (meth)acrylate compound had a weight average molecular weight of 733. The measurement of a weight average molecular weight was performed by using HLC-8120 GPC, produced by Tohso Corporation, equipped with a refractive index detector (RI) as a detector and TSK gel G1000HXL+G2000HXL+G3000HXL+G4000HXL as columns for measurement. The measurement conditions were tetrahydrofuran (THF) as a solvent, a concentration of a specimen controlled to a range of from 0.2 to 0.3%, a column temperature of 40° C. and a flow velocity of 1.0 ml/min.

Comparative Example 1

A reaction mixture was obtained in the same manner as in Example 1 except that the Reynolds number was 0.26. The result of quantitative determination of unreacted acrylic acid in the reaction mixture revealed that epoxy acrylate was formed at a reaction rate of 67.4% with a reaction time of 296 seconds. No runaway reaction occurred.

Comparative Example 2

737 g of a bisphenol A epoxy resin (epoxy equivalent: 189), 277 g of acrylic acid, 5.1 g of triphenylphosphine as a catalyst and 0.5 g of methoquinone as a polymerization inhibitor were charged in a four-neck flask equipped with a thermometer, an agitator, a water-cooled condenser, a nitrogen blowing nozzle and an air blowing nozzle, and the content was heated to 100° C. over 3 hours with care about generation of heat, and continuously reacted at 100° C. for 12 hours. The reaction was terminated at the time when the acid value reached 2 or less, thereby providing epoxy acrylate for comparison.

The weight average molecular weight of the epoxy (meth)acrylate compound measured under the same measurement conditions was 793.

Comparative Example 3

737 g of a bisphenol A epoxy resin (epoxy equivalent: 189), 277 g of acrylic acid, 5.1 g of triphenylphosphine as a catalyst and 0.5 g of methoquinone as a polymerization inhibitor were charged in a four-neck flask equipped with a thermometer, an agitator, a water-cooled condenser, a nitrogen blowing nozzle and an air blowing nozzle, and the content was heated to 100° C. over 30 minutes. Immediately, heat was generated uncontrollably, the content of the flask was gelled, and a large amount of gas was generated from the flask.

The temperature of the temperature controlling liquid for heating the chemical reaction device, the Reynolds number, the reaction time and the reaction rate of the resulting epoxy acrylate of Examples 1 to 5 and Comparative Example 1 are shown in Table 1. It is apparent from Examples and Comparative Example, the relationship of which is shown in FIG. 1., that a larger Reynolds number increases the reaction speed, thereby producing epoxy acrylate with good efficiency.

TABLE 1 Example Example Example Example Example Comparative 1 2 3 4 5 Example 1 Chemical reaction device 40 50 50 50 50 40 Temperature of temperature 180 180 180 180 180 180 controlling liquid (° C.) Reynolds number 1.24 1.75 3.72 7.44 2.62 0.26 Time (sec) 63 135 63 32 90 296 Reaction rate (%) 34.0 86.4 92.3 86.0 99.0 67.4

The synthesis conditions in Comparative Examples 2 and 3 are shown in Table 2 along with the analysis values of the properties in Example 5. The analysis values of the properties of the resulting epoxy acrylate are shown in Table 3 along with the synthesis conditions in Example 5.

TABLE 2 Temperature of Reynolds number Reaction mode Reaction time liquid in microchannel Example 5 continuous mode 90 seconds 180° C. 2.62 in microchannel Comparative batch mode in 15 hours room — Example 2 flask temperature-100° C. Comparative batch mode in several minutes after 200° C. or more due — Example 3 flask increasing temperature to to generation of heat 100° C. over 30 minutes

The analysis values of the properties of the resulting epoxy acrylate are shown in Table 3 along with the analysis values of the properties in Example 5.

TABLE 3 Reaction Result of GPC Presence of rate % measurement runaway reaction Example 5 99.0% weight average molecular none weight Mw: 733 Comparative 99.6% weight average molecular none Example 2 weight Mw: 793 Comparative not not measured occurred Example 3 measured gelation gas generated

It is understood from the reaction conditions shown in Table 1 and the evaluation results shown in FIG. 5 that in the case where the compound (A) and the compound (B) are fed to the microchannel satisfying the particular conditions at the particular flow velocity, it has been considered that owing to the small dimension and the small flow, the reaction proceeds only through spontaneous diffusion behavior of molecules in the flow where a laminar flow is dominant, but it has been found that even in the region of flow where a laminar flow is dominant, a larger Reynolds number provides progress of mixing associated with a microturbulent flow in the channel, contact between the compound (A) and the compound (B) is activated, thereby increasing the reaction speed significantly, and thus the invention has been completed. In Example 5, the reaction is completed in a considerably short period of time without occurrence of runaway reaction. This is a result obtained by such procedures that the compound (A) and the compound (B) are fed to the microchannel satisfying the particular conditions at a flow velocity corresponding to the particular Reynolds number (0.4 or more), and reacted in the microchannel at the reaction temperature (180° C.), which cannot be generally employed by a batch mode reaction, such as a reaction vessel, due to danger of runaway reaction.

Comparative Example 1 shows the results obtained in such a manner that the bisphenol A epoxy resin and acrylic acid are fed to the microchannel at a velocity corresponding to the Reynolds number (less than 0.4), and reacted in the microchannel at the reaction temperature (180° C.), which cannot be generally employed by a batch mode reaction, such as a reaction vessel, due to danger of runaway reaction. It is understood that in the case where the Reynolds number is less than 0.4, even though the reaction is performed for a prolonged period of time at a considerably high reaction temperature, the viscosity of the reaction product is increased associated with the progress of the reaction to lower significantly the mixing property by molecular diffusion, and thus the reaction cannot be performed in a short period of time.

Comparative Example 2 shows the results of the batch mode performed with a reaction vessel. For the purpose of suppressing runaway reaction from occurring and controlling sufficiently the temperature in the system, the temperature is gradually increased over 3 hours after charging the raw materials, and the reaction is performed at a low temperature of 100° C., whereby a period of 15 hours is required until completion of the reaction. It is understood from the results that the results of Example 5 is a safe and efficient production process of an epoxy (meth)acrylate compound.

Comparative Example 3 shows the results obtained in such a manner that the temperature is quickly increased to 100° C. over 30 minutes after charging the raw materials, and the reaction is performed by a batch mode, for shortening the reaction time. After reaching 100° C., heat is generated rapidly, and gelation occurs associated with severe generation of gas. So-called runaway reaction occurs. It is understood from the results that the results of Example 5 is a safe and efficient production process of an epoxy (meth)acrylate compound.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 The figure is a perspective view showing the schematic overall structure of the chemical reaction device including the connecting part used in the production process of the invention.

FIG. 2 The figure is a horizontal cross-sectional view showing the schematic overall structure of the chemical reaction device including the connecting part used in the production process of the invention.

FIG. 3 The figure is a perspective exploded view showing the structures of the two kinds of plates in FIG. 2.

FIG. 4 The figure is a schematic structural view showing schematically the production apparatus used in Examples and Comparative Examples.

FIG. 5 The figure is a graph showing the experimental results of the reaction rate with respect to the transit time in Examples and Comparative Example.

EXPLANATION OF SYMBOLS α liquid containing compound (A) and compound (B) β liquid containing reaction product of compound (A) and compound (B) γ temperature controlling liquid 1 chemical reaction device 1b end surface of chemical reaction device 1c end surface of chemical reaction device 1d side surface of chemical reaction device 1e side surface of chemical reaction device 2 first plate (process plate) 2a surface of first plate 2b end surface of first plate 2c end surface of first plate 2d side surface of first plate 2e side surface of first plate 3 second plate (temperature controlling plate) 3a surface of second plate 3b end surface of second plate 3c end surface of second plate 3d side surface of second plate 3e side surface of second plate 4 channel having concave trench cross-sectional shape 6 temperature controlling channel having concave trench cross-sectional shape 6a main channel having concave trench cross-sectional shape 6b feed-side channel having concave trench cross-sectional shape 6c discharge-side channel having concave trench cross-sectional shape p₀ prescribed interval w₀ width d₀ depth L length of channel 30 connector 31 joint part 32 connecting part 40 chemical reaction device 50 chemical reaction device 60 chemical reaction device 80 production apparatus 61 compound (A) 62 compound (B) 63 syringe pump 64 syringe pump 65 mixer 66 temperature controlling unit 67 cooling heat exchange device 68 temperature controlling unit 69 exhaust pressure valve 70 receiving vessel 80 schematic structural view showing schematically production apparatus of resin used in Examples and Comparative Examples 

The invention claimed is:
 1. A process for preventing a runway reaction in a production of an epoxy (meth)acrylate, comprising causing a mixed liquid of a (meth)acrylic acid and a bisphenol epoxy resin to pass continuously and densely through a tubular microchannel formed in a heat-conducting reaction device, and reacting the carboxyl group of (meth)acrylic acid with the epoxy group of the bisphenol epoxy resin, the tubular microchannel in the reaction device having a space size making a fluid cross-sectional area, through which the mixed liquid passes densely, of from 0.1 to 4.0 mm², and the process comprising heating the heat-conducting reaction device to a temperature of from 170 to 220° C., reacting the mixed liquid to provide a Reynolds number of a reaction liquid passing through the tubular microchannel in a range of from 0.4 to 100, and after completing reaction, cooling continuously a reaction product discharged from the heat-conducting reaction device.
 2. The process for preventing a runway reaction in a production of an epoxy (meth)acrylate according to claim 1, wherein the reaction product after completing reaction is cooled under a temperature condition of from 50 to 90° C.
 3. The process for preventing a runway reaction in a production of an epoxy (meth)acrylate according to claim 1, wherein (meth)acrylic acid and the bisphenol epoxy resin are mixed in advance to form a mixed liquid, and the mixed liquid is fed continuously to the heat-conducting reaction device.
 4. The process for preventing a runway reaction in a production of an epoxy (meth)acrylate according to claim 3, wherein reaction is performed by using a reaction apparatus containing a plurality of the heat-conducting reaction devices connected in series each having the tubular microchannel formed therein.
 5. The process for preventing a runway reaction in a production of an epoxy (meth)acrylate according to claim 3, wherein the heat-conducting reaction device having the tubular microchannel formed therein has a structure containing a plurality of heat-conducting plate structures each having plural trenches on a surface thereof, which are laminated on each other.
 6. The process for preventing a runway reaction in a production of an epoxy (meth)acrylate according to claim 1, wherein the mixed liquid is caused to pass through the tubular microchannel at a flow velocity of from 1.8×10⁻⁴ to 0.28 msec.
 7. The process for preventing a runway reaction in a production of an epoxy (meth)acrylate according to claim 1, wherein the continuous cooling is performed by causing the reaction product to pass continuously through a cooling heat exchange device having a tubular microchannel formed therein connected to an exit of a reaction liquid of the heat-conducting reaction device.
 8. The process for preventing a runway reaction in a production of an epoxy (meth)acrylate according to claim 2, wherein the (meth)acrylic acid and the bisphenol epoxy resin are mixed in advance to form a mixed liquid, and the mixed liquid is fed continuously to the heat-conducting reaction device.
 9. The process for preventing a runway reaction in a production of an epoxy (meth)acrylate according to claim 8, wherein reaction is performed by using a reaction apparatus containing a plurality of the heat-conducting reaction devices connected in series each having the tubular microchannel formed therein.
 10. The process for preventing a runway reaction in a production of an epoxy (meth)acrylate according to claim 8, wherein the heat-conducting reaction device having the tubular microchannel formed therein has a structure containing a plurality of heat-conducting plate structures each having plural trenches on a surface thereof, which are laminated on each other.
 11. The process for preventing a runway reaction in a production of an epoxy (meth)acrylate according to claim 2, wherein the continuous cooling is performed by causing the reaction product to pass continuously through a cooling heat exchange device having a tubular microchannel formed therein connected to an exit of a reaction liquid of the heat-conducting reaction device. 